Product Features of zirconia block:
♠ 6 layers Multilayer color
♠ From 43% to 57% gradient for transparency
♠ Strength shows gradient from 10500 Mpa to 700 Mpa
♠ Suitable for anterior, crown, 7 unit bridges and all restoration
Indication of dental zirconia block:
Crown /Inlay /Onlay /Implant /Anterior/Posterior/Veneer
| Sintered Density |
6.07 ± 0.03g/cm3 |
| Hardness |
1200HV |
| Sintering Temperature |
Recommend 1500℃ |
| Bending Strength |
1050Mpa-700Mpa |
| Translucency |
43%-57% |
Advantage of dental zirconia:
Safety: No irritation,No corrosion,Good bio-compatibility
Beauty: Natural teeth color can be reproduced
Comfortability: Low thermal conductivity,hot and cold changes do not stimulte the pulp
Durability: Over 1600MPa perturbed strength, durable and useful
As the leading manufacturer of dental zirconia block in china, Yucera zirconia block includes white zirconi block(HT, ST, UT), pre-shaded zirconia block (ST-color,) and multilayer preshaded zirconia block(SHT, UTMultilayer, 3D Plus Multilayer).
| Type |
Code |
Translucency |
Bending Strength |
Hardness |
Color |
size |
| white zirconia block |
HT |
40% |
≥1200Mpa(Av.) |
1200HV |
white (coloring liquid with vita 16 shades and 26 shades |
Open system & Zirkon zahn system (D98*10-25mm & D95*10-25mm |
| white zirconia block |
ST |
43% |
≥1200Mpa(Av.) |
1200HV |
same as above |
same as above |
| Shade zirconia block |
ST-color |
43% |
≥1100Mpa(Av.) |
1200HV |
Vita 16 shades and BL1, BL2, BL3, BL4 |
same as above |
| Multi zirconia block |
SHT-ML |
46% |
≥900Mpa(Av.) |
1200HV |
same as above |
same as above |
| Multi zirconia block |
UT-ML |
49% |
≥600Mpa(Av.) |
1200HV |
same as above |
same as above |
| Multi zirconia block |
3D Plus-ML |
43%-57% |
≥10500Mpa(Av.)-≥700Mpa(Av.) |
1200HV |
same as above |
same as above |